Sodium Na Ion Battery Separator Battery Raw Materials For Coin Cell Battery Research

Product Categories

Shandong Gelon Lib Co., Ltd

Contact Now

Sodium Na Ion Battery Separator Battery Raw Materials For Coin Cell Battery Research

Name: Sodium Na Ion Battery Separator Battery Raw Materials For Coin Cell Battery Research
Brand: Gelon
Price: 1.00 USD

Best Sodium Na Ion Battery Separator Battery Raw Materials For Coin Cell Battery Research wholesale

Brand Name : Gelon

Certification : CE

Place of Origin : China

MOQ : 1square

Price : $1.00 - $3.00/ square meter |1 square meter/square meters(Min. Order)

Payment Terms : L/C, D/A, D/P, T/T, Western Union, MoneyGram

Supply Ability : 1000square

Delivery Time : 15days

Packaging Details : Standard exported package : Internal anticollision protection, external export wooden box packaging.

Warranty : 3months-1year

Battery Size : Lithium ion battery

Model Number : GN-Separator

Weight : 3kg/roll

Appearance : White

Thickness : 5um to 25um customize

MD tensile strength : ≥150

Material : PE /PE or multi layers

Use for : Battery seperator

Type : PP or PE or Ceramic coated

Width : customize

Contact Now

Sodium Na ion Battery Separator Battery Raw Materials for Coin cell Battery ResearchProduct

Product Description
PE PP PP/PE/PP Multi layers Battery Separator with Customized Width 
 
 PE & PP separators are used for lithium-ion battery manufacturers and researchers. The materials consist of Polymer film , that are either Polypropylene (PP) or Polyethylene (PE) based. contain micro and nano pores to provide excellent ion transportation capabilities within the li-ion battery.
Also Ceramic-coated variety for enhanced thermal deformation resistance and mechanical strength.
Specification
 	 			No.
 			Test Term
 			Unit
 			Inspection value
 		
 			1
 			Thickness
 			micron
 			20.0±2.0
 		
 			2
 			Surface density
 			g/㎡
 			17.0±2.0
 		
 			3
 			Ceramic layer Surface density
 			g/㎡
 			8.0±1.5
 		
 			4
 			Gas permeability
 			Sec/100ml
 			250±40
 		
 			5
 			Gas permeability increment
 			%
 			≤15%
 		
 			6
 			Puncturing Strength
 			gf
 			≥580
 		
 			7
 			120℃ *1h shrinking percentage
 			MD
 			%
 			≤2.0
 		
 			8
 			TD
 			%
 			≤1.5
 		
 			9
 			Tensile strength
 			MD
 			Mpa
 			≥150
 		
 			10
 			TD
 			Mpa
 			≥135
 		
 			11
 			Tensile
 			Elongation
 			MD
 			%
 			≥50
 		
 			12
 			TD
 			%
 			≥50
 		
 			13
 			Film close temperature
 			℃
 			≤135
 		
 			14
 			Width
 			mm
 			 
 		
 			15
 			Length
 			m
 			 
 		
 			16
 			Peel strength
 			N/m
 			≥40
 		
 			17
 			Static electricity
 			KV
 			≤2.0
 		
 			18
 			Water content
 			ppm
 			≤1200
 		
  

Product Tags:

Sodium Na ion Battery Separator

Coin cell Battery Raw Materials

lithium ion battery separator

Sodium Na Ion Battery Separator Battery Raw Materials For Coin Cell Battery Research Images

Inquiry Cart 0

Send your message to this supplier


*From:	Your email address is incorrect!
*To:	Shandong Gelon Lib Co., Ltd
*Subject:	Subject is empty!
*Message:	For the best results, we recommend including the following details: -Self introduction -Required specifications -Inquire about price/MOQ Characters Remaining: (0/3000) Please enter 20 to 3000 characters to contact this supplier!

No.	Test Term		Unit	Inspection value
1	Thickness		micron	20.0±2.0
2	Surface density		g/㎡	17.0±2.0
3	Ceramic layer Surface density		g/㎡	8.0±1.5
4	Gas permeability		Sec/100ml	250±40
5	Gas permeability increment		%	≤15%
6	Puncturing Strength		gf	≥580
7	120℃ *1h shrinking percentage	MD	%	≤2.0
8	120℃ *1h shrinking percentage	TD	%	≤1.5
9	Tensile strength	MD	Mpa	≥150
10	Tensile strength	TD	Mpa	≥135
11	Tensile Elongation	MD	%	≥50
12	Tensile Elongation	TD	%	≥50
13	Film close temperature		℃	≤135
14	Width		mm
15	Length		m
16	Peel strength		N/m	≥40
17	Static electricity		KV	≤2.0
18	Water content		ppm	≤1200